Please use this identifier to cite or link to this item: http://bura.brunel.ac.uk/handle/2438/14887
Title: Synthesis, characterization, and performance evaluation of multilayered photoanodes by introducing mesoporous carbon and TiO<inf>2</inf>for humic acid adsorption
Authors: Hosseini, S
Jahangirian, H
Webster, TJ
Masoudi Soltani, S
Arou, MK
Keywords: renewable energy;photocatalysis;mesoporous carbon;TiO2 nanoparticle;multilayer photoelectrode;humic acid
Issue Date: 16-Aug-2016
Publisher: Dove Medical Press
Citation: Hosseini, S. et al. (2016) 'Synthesis, characterization, and performance evaluation of multilayered photoanodes by introducing mesoporous carbon and TiO<inf>2</inf>for humic acid adsorption', International Journal of Nanomedicine, 11: pp. 3969 - 3978. doi: 10.2147/IJN.S96558.
Abstract: Copyright © 2016 The Author(s). Nanostructured photoanodes were prepared via a novel combination of titanium dioxide (TiO2) nanoparticles and mesoporous carbon (C). Four different photoanodes were synthesized by sol-gel spin coating onto a glassy substrate of fluorine-doped tin oxide. The photocatalytic activities of TiO2, TiO2/C/TiO2, TiO2/C/C/TiO2, and TiO2/C/TiO2/C/TiO2photoanodes were evaluated by exposing the synthesized photoanodes to UV-visible light. The photocurrent density observed in these photoanodes confirmed that an additional layer of mesoporous carbon could successfully increase the photocurrent density. The highest photocurrent density of ∼1.022 mA cm−2at 1 V/saturated calomel electrode was achieved with TiO2/C/C/TiO2under an illumination intensity of 100 mW cm−2from a solar simulator. The highest value of surface roughness was measured for a TiO2/C/C/TiO2combination owing to the presence of two continuous layers of mesoporous carbon. The resulting films had a thickness ranging from 1.605 μm to 5.165 μm after the calcination process. The presence of double-layer mesoporous carbon resulted in a 20% increase in the photocurrent density compared with the TiO2/C/TiO2combination when only a single mesoporous carbon layer was employed. The improved performance of these photoanodes can be attributed to the enhanced porosity and increased void space due to the presence of mesoporous carbon. For the first time, it has been demonstrated here that the photoelectrochemical performance of TiO2can be improved by integrating several layers of mesoporous carbon. Comparison of the rate of removal of humic acid by the prepared photoanodes showed that the highest performance from TiO2/C/C/TiO2was due to the highest photocurrent density generated. Therefore, this study showed that optimizing the sequence of mesoporous carbon layers can be a viable and inexpensive method for enhanced humic acid removal.
URI: https://bura.brunel.ac.uk/handle/2438/14887
DOI: https://doi.org/10.2147/IJN.S96558
ISSN: 1176-9114
Appears in Collections:Dept of Chemical Engineering Research Papers

Files in This Item:
File Description SizeFormat 
FullText.pdfCopyright © 2016 The Author(s). This work is published and licensed by Dove Medical Press Limited. The full terms of this license are available at https://www.dovepress.com/terms.php and incorporate the Creative Commons Attribution - Non Commercial (unported, v3.0) License. By accessing the work you hereby accept the Terms. Non-commercial uses of the work are permitted without any further permission from Dove Medical Press Limited, provided the work is properly attributed. For permission for commercial use of this work, please see paragraphs 4.2 and 5 of our Terms.4.19 MBAdobe PDFView/Open


This item is licensed under a Creative Commons License Creative Commons